Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | % | 1.7 -- |
| Shrinkage rate | | % | 2.3 -- |
| Water absorption rate | | % | 3.0 -- |
| Water absorption rate | | % | 0.50 -- |
| density | | g/cm³ | 1.03 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | MPa | 50.0 35.0 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | | HB -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Charpy Notched Impact Strength | | kJ/m² | 15 15 |
| Charpy Notched Impact Strength | | | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | MPa | 750 450 |
| tensile strength | Break | MPa | 40.0 40.0 |
| Tensile strain | Break | % | >50 >50 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | V | -- |
| Volume resistivity | | ohms·cm | 1E+11 1E+12 |
| dielectric strength | | kV/mm | 38 37 |
| Surface Resistivity | | ohms | -- 1E+11 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | °C | 215 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 2E-04 -- |
| Heat distortion temperature | | °C | 115 -- |
| Heat distortion temperature | | °C | 50.0 -- |
| Continuous use temperature | | °C | 110to130 -- |
| Continuous use temperature | | °C | 160 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.5E-04 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare