PA6 73G35HSL BK262 DUPONT SHENZHEN

Form：Granules | Grade：Injection grade

Properties:

lubricationHigh temperature resistanFiller: Glass fiber reinf35% filler by weight

Typical Applications:

Automotive componentsElectronic and Electrical Applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive components \| Electronic and Electrical Applications
Properties:	lubrication \| High temperature resistan \| Filler: Glass fiber reinf \| 35% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	3.00	J
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	24	mm/min
FMVSS flammability		FMVSS302	B
Flammability level	1.5mm	IEC 60695-11-10,-20	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	280	Mpa
Bending modulus		ISO 178	9900	Mpa
Tensile strain	Break	ISO 527-2	3.2	%
tensile strength	Break	ISO 527-2	190	Mpa
Tensile modulus		ISO 527-2	11000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	2E-05	cm/cm/°C
Melting temperature		ISO 11357-3	221	°C
Vicat softening temperature		ISO 306/B50	215	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	208	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	ISO 294-4	1.0	%
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	1.8	%
Water absorption rate	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	5.8	%
Shrinkage rate	MD	ISO 294-4	0.20	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.