PA6 YH-900 SINOPEC BALING
118
- Properties:Medium viscosityMedium viscosity
- Usages:MonofilamentSuitable for general injection moldingExtrusion moldingFlame retardant modification and spinning of brownMonofilamentetc
CompareTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| relative viscosity | GB/T 1632-93 | 2.90±0.03 --- | |
| density | GB 1033-86 | 1.157 g/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | GB/T 1043-93 | 1.40 % | |
| Shore hardness | GB 9341-88 | 63.8 R | |
| elongation at break | GB 1040-92 | 153.4 % | |
| Impact strength of cantilever beam gap | IEC (CTI) | 22.4 KJ/m | |
| Flexural modulus | GB 9341-88 | 2026 Mpa | |
| bending strength | GB 9341-88 | 83.6 Mpa | |
| tensile strength | GB 1040-92 | 66.5 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | GB 1044-70 | 1.3 --- | |
| Surface Resistivity | GB 1044-70 | 5.7×10 Ω | |
| GB 1044-70 | 8.0×10 Ω | ||
| Volume resistivity | GB 1044-70 | 7.2×10 Ω | |
| Dielectric loss | GB 1044-70 | 4.3×10 | |
| Volume resistivity | GB 1044-70 | 6.7×10 Ω.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 217～223 °C | ||
| Heat distortion temperature | 74.1 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.