Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | | 0.20 % |
| Shrinkage rate | | | 0.50 % |
| Water absorption rate | | ASTM D570 | 0.020 % |
| density | | ASTM D792 | 1.69 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 102 |
| Rockwell hardness | | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-05VA |
| Limiting Oxygen Index | | ASTM D2863 | 53 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 260 Mpa |
| compressive strength | | ASTM D695 | 285 Mpa |
| Poisson's ratio | | | 0.39 |
| tensile strength | | ASTM D638 | 179 Mpa |
| tensile strength | | ISO 527-2 | 180 Mpa |
| elongation | | ASTM D638 | 1.5 % |
| Tensile strain | | ISO 527-2 | 1.4 % |
| Flexural modulus | | ASTM D790 | 14500 Mpa |
| Flexural modulus | | ISO 178 | 14000 Mpa |
| bending strength | | ASTM D790 | 255 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 80 J/m |
| Impact strength of cantilever beam gap | | ISO 180/A | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTM D4812 | 510 J/m |
| Suspended wall beam without notch impact strength | | ISO 180 | 30 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | ASTM D150 | 2E-03 |
| Dissipation Factor | | ASTM D150 | 3E-03 |
| arc resistance | | ASTM D495 | 125 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 4 |
| insulation resistance | | | 1E+11 ohms |
| Volume resistivity | | ASTM D257 | 1E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 22 KV/mm |
| dielectric constant | | ASTM D150 | 3.80 |
| dielectric constant | | ASTM D150 | 3.90 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTME831 | 2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 1.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 4E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 0.30 W/m/K |
| UL temperature rating | | UL 746B | 200to220 °C |
| Heat distortion temperature | | ASTM D648 | 265 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.