Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.32 g/cm³ |
| Shrinkage rate | | ASTMD1204 | 0.50到0.70 % |
| surface tension | | | >38 mN/m |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Pencil Hardness | | | 2B-B |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0VTM-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 65.0 MPa |
| Tensile strain | Break | ISO527-2 | >100 % |
| Flexural modulus | | ISO178 | 2200 MPa |
| Bending stress | | ISO178 | 91.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTMD257 | 1E+16 ohms |
| Volume resistivity | | ASTMD257 | 1E+17 ohms·cm |
| dielectric strength | | ASTMD149 | 59 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | ISO11357-2 | 153 °C |
| vicat | | ISO11357 | 156 °C |
| | ISO11359-2 | 5.8E-05 cm/cm/°C |
| thermal conductivity | | ASTMD5470 | 0.20 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.