Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.20to0.50 % |
| density | | ASTM D792 | 1.27 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 108 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ASTM D1003 | 0.20 % |
| transmissivity | | ASTM D1003 | 90.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2030 MPa |
| Tensile modulus | | ISO 527-2 | 2000 MPa |
| tensile strength | | ASTM D638 | 50.0 MPa |
| tensile strength | | ISO 527-2 | 48.0 MPa |
| tensile strength | | ASTM D638 | 30.0 MPa |
| tensile strength | | ISO 527-2 | 29.0 MPa |
| elongation | | ASTM D638 | 4.4 % |
| elongation | | ISO 527-2 | 4.0 % |
| elongation | | ASTM D638 | 180 % |
| elongation | | ISO 527-2 | 200 % |
| Flexural modulus | | ASTM D790 | 2060 MPa |
| Flexural modulus | | ISO 178 | 2100 MPa |
| bending strength | | ASTM D790 | 68.0 MPa |
| bending strength | | ISO 178 | 67.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 40 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 110 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 4.4 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 9.4 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTM D256 | 无断裂 |
| Suspended wall beam without notch impact strength | | ASTM D256 | 无断裂 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 70.0 °C |
| Heat distortion temperature | | ASTMD648 | 62.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.