PC EXL1414-GY7D493 SABIC INNOVATIVE KOREA

Form：Granules | Grade：Injection grade

Properties:

ProcessabilityModerate liquidityDuctilitycopolymerGood demolding performanc

Typical Applications:

currencyElectrical fieldElectronic field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	currency \| Electrical field \| Electronic field
Properties:	Processability \| Moderate liquidity \| Ductility \| copolymer \| Good demolding performanc

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ASTM D256	870	J/m
Dart impact	23°C, Total Energy	ASTM D3763	70.0	J
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Impact strength of cantilever beam gap	-30°C	ASTM D256	770	J/m
	Impact strength of cantilever beam gap	-30°C8	ISO 180/1A	60	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C8	ISO 180/1A	70	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	70	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	65	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40 mm	UL 94	HB
Burning wire flammability index	0.8 mm	IEC 60695-2-12	850	°C
Burning wire flammability index	Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	875	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	875	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	--5,6	ISO 178	85.0	Mpa
bending strength	bending strength	Yield, 50.0 mm Span4	ASTM D790	92.0	Mpa
Bending modulus	50.0 mm Span4	ASTM D790	2230	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2250	Mpa
elongation	Break	ISO 527-2/50	120	%
tensile strength	Break3	ASTM D638	50.0	Mpa
	tensile strength	Yield	ISO 527-2/50	57.0	Mpa
	tensile strength	tensile strength	Yield3	ASTM D638	55.0	Mpa
Tensile modulus	--	ISO 527-2/1	2150	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2020	Mpa
elongation	Break3	ASTM D638	98	%
	elongation	Yield	ISO 527-2/50	6.0	%
	elongation	elongation	Yield3	ASTM D638	6.0	%
tensile strength	Break	ISO 527-2/50	60.0	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Processing (melt) temperature			295 to 315	°C
Spray nozzle temperature			290 to 310	°C
Temperature at the front of the material cylinder			295 to 315	°C
Temperature in the middle of the barrel			280 to 305	°C
Temperature at the rear of the barrel			270 to 295	°C
Suggested injection volume			40 to 60	%
Suggested maximum moisture content			0.020	%
drying time			3.0 to 4.0	hr
drying temperature			120	°C
Back pressure			0.300 to 0.700	Mpa
Mold temperature			70 to 95	°C
Exhaust hole depth			0.025 to 0.076	mm
Screw speed			40 to 70	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Elec		UL 746	130	°C
RTI Imp		UL 746	120	°C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.2E-5	cm/cm/°C
RTI		UL 746	125	°C
Vicat softening temperature	--	ASTM D152510	145	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	128	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Be	140	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	124	°C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	139	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.2E-5	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	146	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	--	ISO 1183	1.19	g/cm³
density	density	--	ASTM D792	1.18	g/cm³
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	9.00	cm3/10min
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	10	g/10 min
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.35	%
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.40 - 0.80	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.80	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1 MHz	ASTM D150	9.3E-3
Dissipation factor	Dissipation factor	100 Hz	ASTM D150	1.2E-3
Dielectric constant	1 MHz	ASTM D150	2.64
Volume resistivity		ASTM D257	> 1.0E+15	ohms·cm
Surface resistivity		ASTM D257	> 1.0E+15	ohms
Dielectric constant	100 Hz	ASTM D150	2.68
Dielectric strength	0.800 mm, in Oil	ASTM D149	16	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	L -Sale	ASTM D785	89
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	121

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.