PA66

PA66 VENYL ZG307 - 7761 AD MAJORIS FRANCE

Properties:
Filler glass fiber reinforced material 30% filler by weight
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	80 kJ/m²
Charpy Notched Impact Strength		ISO 179	11 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	235 MPa
Bending modulus		ISO 178	8300 MPa
Tensile strain	Break	ISO 527-2	3.0 %
Tensile strain	Tensile strain	Yield	ISO 527-2	3.0 %
tensile strength	Break	ISO 527-2	185 MPa
Tensile modulus		ISO 527-2	9800 MPa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	DIN 52328	3E-05 cm/cm/°C
Melting temperature		ISO 3146	242 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	230 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	235 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr	ISO 62	0.95 %
Shrinkage rate			0.50to0.70 %
density		ISO 1183	1.37 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.