Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Outdoor applicability | | UL 746C | f1 |
| density | | ASTM D792 | 1.25 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 7.6 g/10min |
| melt mass-flow rate | | ASTM D1238 | 7.6 g/10min |
| Melt volume flow rate | | ISO 1133 | 6.80 cm³/10min |
| Melt volume flow rate | | ISO 1133 | 6.80 cm³/10min |
| Shrinkage rate | | 内部方法 | 0.50to0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | 5VA |
| UL flame retardant rating | | UL 94 | YES |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| fracture | | ISO 527-2 | 57.1 MPa |
| yield | | ASTM D638 | 3.8 % |
| yield | | ISO 527-2 | 3.7 % |
| fracture | | ASTM D638 | 8.4 % |
| fracture | | ISO 527-2 | 11 % |
| yield | | ASTM D790 | 117 MPa |
| fracture | | ASTM D790 | 117 MPa |
| yield | | ISO 527-2 | 71.7 MPa |
| fracture | | ASTM D638 | 60.0 MPa |
| yield | | ASTM D638 | 74.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/2C | 10 kJ/m² |
| Suspended wall beam without notch impact strength | | ASTM D4812 | 2200 J/m |
| Reverse notch impact | | ASTM D256 | 810 J/m |
| Dart impact | | ASTM D3763 | 443 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | ASTM D257 | >1.0E+16 ohms |
| Volume resistivity | | ASTM D257 | 1.2E+16 ohms·cm |
| dielectric strength | | ASTM D149 | 17 kV/mm |
| dielectric constant | | ASTM D150 | 2.89 |
| dielectric constant | | ASTM D150 | 2.89 |
| dielectric constant | | ASTM D150 | 2.70 |
| Dissipation Factor | | ASTM D150 | 0.017 |
| Dissipation Factor | | ASTM D150 | 0.017 |
| Dissipation Factor | | ASTM D150 | 4.4E-03 |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 2 |
| High arc combustion index (HAI) | | UL 746 | PLC 2 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Imp | | UL 746 | 85.0 °C |
| RTI | | UL 746 | 100 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 7.1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 7.8E-05 cm/cm/°C |
| RTI Elec | | UL 746 | 100 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare