POM Homopolymer

POM Homopolymer 300TE BK602 DUPONT USA

0

Technical Data Sheet

physical property Test ConditionTest MethodTest Result
densityISO 11831.37 g/cm³
melt mass-flow rateISO 11336.0 g/10min
MediumDensity1.15 g/cm³
Melt volume flow rateISO 11334.30 cm³/10min
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessISO 2039-269
Rockwell hardnessR-ScaleISO 2039-2116
flammabilityTest ConditionTest MethodTest Result
burning rateISO 3795<100 mm/min
FMVSS flammabilityFMVSS302B
Supplementary InformationTest ConditionTest MethodTest Result
EmissionVDA275<2.00 mg/kg
Impact resistanceTest ConditionTest MethodTest Result
Charpy Notched Impact StrengthISO 179/1eA8.0 kJ/m²
Charpy Notched Impact StrengthISO 179/1eA15 kJ/m²
Impact strength of simply supported beam without notchISO 179/1eU150 kJ/m²
Impact strength of simply supported beam without notchISO 179/1eUNoBreak
Mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-22100 MPa
tensile strength YieldISO 527-255.0 MPa
Tensile strainYieldISO 527-220 %
Nominal tensile fracture strainISO 527-225 %
Flexural modulusISO 1782000 MPa
bending strengthISO 17855.0 MPa
Thermal performanceTest ConditionTest MethodTest Result
Heat distortion temperatureISO 75-2/B136 °C
Heat distortion temperatureISO 75-2/A78.0 °C
Linear coefficient of thermal expansionISO 11359-21.1E-04 cm/cm/°C
Linear coefficient of thermal expansionISO 11359-21.2E-04 cm/cm/°C
AnnealingTemperature160 °C
AnnealingTime-Optional30.0 min/mm
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.