'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PBT VX4920 SABIC INNOVATIVE US
28
Form：Granules | Grade：Injection grade
Properties:
High mobilityHigh crystallinityAging resistanceFiller: Glass fiber reinf20%Filler by weight
Typical Applications:
engineering application Automotive componentsElectronic and electrical componentsLaptop caseApplication in the automotive field
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | engineering application | Automotive components | Electronic and electrical components | Laptop case | Application in the automotive field |
| Properties: | High mobility | High crystallinity | Aging resistance | Filler: Glass fiber reinf | 20% | Filler by weight |
Certificates
No Data...
Technical Data Sheet
| Filling analysis | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C,1500sec^-1 | ISO 11443 | 175 | Pa·s |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 50.0 | J |
| 23°C | ISO 180/1U | 45 | kJ/m² | |
| -30°C | ISO 180/1U | 40 | kJ/m² | |
| 23°C | ASTM D4812 | 680 | J/m | |
| -30°C | ASTM D4812 | 610 | J/m | |
| 23°C | ISO 180/1A | 7.0 | kJ/m² | |
| 0°C | ISO 180/1A | 7.0 | kJ/m² | |
| -30°C | ISO 179/1eA | 5.0 | kJ/m² | |
| 23°C | ISO 179/1eU | 45 | kJ/m² | |
| ISO 179/2U | 55 | kJ/m² | ||
| -30°C | ISO 179/2C | 8.0 | kJ/m² | |
| 23°C | ISO 179/1eA | 6.0 | kJ/m² | |
| ISO 179/2C | 10 | kJ/m² | ||
| -30°C | ISO 179/1eU | 40 | kJ/m² | |
| ASTM D256 | 70 | J/m | ||
| ISO 180/1A | 7.0 | kJ/m² | ||
| 0°C | ASTM D256 | 75 | J/m | |
| 23°C | ASTM D256 | 80 | J/m | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.60mm | UL 94 | HB | |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 750 | °C |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| yield | ISO 527-2/5 | 3.0 | % | |
| ASTM D638 | 3.0 | % | ||
| crack | ISO 527-2/5 | 105 | Mpa | |
| ASTM D638 | 105 | Mpa | ||
| yield | ISO 527-2/5 | 105 | Mpa | |
| ASTM D638 | 90.0 | Mpa | ||
| --3 | ASTM D638 | 7200 | Mpa | |
| crack | ASTM D638 | 3.0 | % | |
| ISO 527-2/5 | 3.0 | % | ||
| 50.0mm span | ASTM D790 | 5500 | Mpa | |
| --9 | ISO 178 | 5700 | Mpa | |
| --10 | ISO 178 | 155 | Mpa | |
| Yield, 50.0mm span | ASTM D790 | 135 | Mpa | |
| Fracture, 50.0mm span | ASTM D790 | 160 | Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | Internal Method | 80.0 | mg |
| Fracture bending strain | ISO 178 | 4.0 | % | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| 0.45MPa, unannealed, 64.0mm span | ISO 75-2/Bf | 210 | °C | |
| 0.45MPa, unannealed, 100mm span | ISO 75-2/Be | 209 | °C | |
| 0.45MPa, unannealed, 3.20mm | ASTM D648 | 210 | °C | |
| Flow: 23 to 150 ° C | 23to150℃ | ISO 11359-2 | 2.4E-05 | cm/cm/°C |
| Horizontal: -40 to 40 ° C | Across Flow, -40to40℃ | ASTME831 | 1.1E-04 | cm/cm/°C |
| Across Flow, -40to40℃ | ISO 11359-2 | 7.7E-05 | cm/cm/°C | |
| Horizontal: 23 to 60 ° C | Across Flow, 23to60℃ | ISO 11359-2 | 1.1E-04 | cm/cm/°C |
| Horizontal: 23 to 150 ° C | Across Flow, 23to150℃ | ISO 11359-2 | 1.6E-04 | cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.25 | W/m/K | |
| 1.8MPa, unannealed, 3.20mm | ASTM D648 | 170 | °C | |
| 1.8MPa, unannealed, 100mm span | ISO 75-2/Ae | 179 | °C | |
| 1.8MPa, unannealed, 64.0mm span of | ISO 75-2/Af | 170 | °C | |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass | |
| Flow: -40 to 40 ° C | ASTME831 | 3E-05 | cm/cm/°C | |
| ISO 11359-2 | 2.9E-05 | cm/cm/°C | ||
| Flow: 23 to 60 ° C | 23to60℃ | ISO 11359-2 | 3E-05 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | MD1 | Internal Method | 0.20-0.40 | % |
| MD:3.20mm | Internal Method | 0.30-0.60 | % | |
| Melt Volume Flow Rate (MVR) | 265°C/5.0kg | ISO 1133 | 30.0 | cm3/10min |
| 250°C/5.0kg | ISO 1133 | 17.0 | cm3/10min | |
| melt mass-flow rate | 265°C/5.0kg | ASTM D1238 | 35 | g/10min |
| 200°C/3.8kg | ASTM D1238 | 17 | g/10min | |
| density | ASTMD792 | 1.38 | g/cm³ | |
| Shrinkage rate | TD2 | Internal Method | 0.40-0.80 | % |
| Water absorption rate | Saturation,23°C | ISO 62 | 0.76 | % |
| Equilibrium,23°C,50%RH | ISO 62 | 0.27 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257 | >1.0E+15 | ohms·cm | |
| 1.60mm,inOil | ASTM D149 | 28 | KV/mm | |
| 1MHz | 1MHz | ASTMD150 | 3.40 | |
| 50Hz | 50Hz | IEC 60250 | 3.40 | |
| 3.20mm, inoil | ASTM D149 | 24 | KV/mm | |
| 1.60mm, in oil | IEC 60243-1 | 28 | KV/mm | |
| 3.20mm, in oil | IEC 60243-1 | 24 | KV/mm | |
| 60Hz | 60Hz | IEC 60250 | 3.40 | |
| 1MHz | 1MHz | ASTMD150 | 0.020 | |
| 50Hz | 50Hz | IEC 60250 | 2.4E-03 | |
| 60Hz | 60Hz | IEC 60250 | 2.4E-03 | |
| Compared to the anti leakage trace index | CTI | UL 746 | PLC 1 | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Ball Pressure Test | H358/30 | ISO 2039-1 | 130 | Mpa |
| Rockwell hardness | R-Sale | ISO 2039-2 | 118 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| Filling material | ASTM D229 | 20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.