TPV 101-73 CELANESE USA

125

Form：Granules | Grade：Injection grade

Properties:
High temperature resistanAging resistanceFlame retardant
Typical Applications:
Fitness equipmentAutomotive ApplicationsElectrical applicationsApplication in the automotive fieldpackingPipe fittingsHome appliance componentsConsumer product application fieldParts under the hood of a carOutdoor applicationsWasherElectrical componentsdiaphragm
Supplier(1)
Product Description
Certificates(0)
Datasheet

Product Description

Typical Applications:Fitness equipment | Automotive Applications | Electrical applications | Application in the automotive field | packing | Pipe fittings | Home appliance components | Consumer product application field | Parts under the hood of a car | Outdoor applications | Washer | Electrical components | diaphragm
Properties:High temperature resistan | Aging resistance | Flame retardant

Certificates

No Data...

Technical Data Sheet

flammabilityTest ConditionTest MethodTest ResultTest Unit
UL flame retardant rating3.0mmUL 94HB
UL flame retardant rating1.5mmUL 94HB
UL flame retardant rating1.0mmUL 94HB
elastomerTest ConditionTest MethodTest ResultTest Unit
tensile strengthBreak,23°CISO 378.80Mpa
tensile strengthBreak,23°C，横向FlowASTM D4128.80Mpa
Tensile stress100%Strain,23°C，横向FlowISO 373.60Mpa
Tensile stress100%Strain,23°C，横向FlowASTM D4123.60Mpa
elongationBreak,23°C，Across FlowASTM D412490%
elongationBreak,23°C，Across FlowISO 37490%
tear strength23°C，横向FlowASTM D62427.0kN/m
tear strength23°C，Across Flow (Across Flow)ISO 34-127kN/m
Permanent compression deformation70°C,22hrASTM D395B28%
Permanent compression deformation125°C,70hrASTM D395B37%
Permanent compression deformation70°C,22hrISO 81528%
Permanent compression deformation125°C,70hrISO 81537%
thermal performanceTest ConditionTest MethodTest ResultTest Unit
RTI ElecUL 74690.0°C
RTI Str1.0mmUL 74690.0°C
Brittle temperatureASTM D746-60.0°C
RTI Str1.5mmUL 74690.0°C
RTI Str3.0mmUL 74695.0°C
Brittle temperatureISO 812-60.0°C
Physical propertiesTest ConditionTest MethodTest ResultTest Unit
Resistance to cleaning agentsUL 749f3
Resistance to cleaning agentsISO 188f4
Outdoor applicabilityUL 746Cf1
Electrical performanceTest ConditionTest MethodTest ResultTest Unit
Dielectric strength23°C,2.00mmASTM D14927KV/mm
Dielectric constant23°C,1.98mmASTM D1502.50
Dielectric constant23°C,1.98mmIEC 602502.50
Compared to the anti leakage trace indexCTIUL 746PLC 0
Hot wire ignition1.0mmUL 746PLC 4
Hot wire ignition1.5mmUL 746PLC 3
Hot wire ignition3.0mmUL 746PLC 3
High arc combustion indexHAIUL 746PLC 0
High voltage arc tracing rateHVTRUL 746PLC 1
hardnessTest ConditionTest MethodTest ResultTest Unit
Shore hardnessShoreA,15Sec,23°CISO 86878
agingTest ConditionTest MethodTest ResultTest Unit
Shore hardnessShoreA,23°C,168hr,inSulfuricAcid,98%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inTrichloroethyleneISO 1817-3.0
Shore hardnessShoreA,100°C,168hr,inDeionizedWaterISO 1817-2.0
Shore hardnessShoreA,23°C,168hr,inSodiumHydroxide,50%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inSodiumChloride,15%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inMethylethylketoneISO 18170.0
Shore hardnessShoreA,23°C,168hr,inIsopropylAlcoholISO 1817-1.0
Tensile stress change rate23°C,168hr,inEthanol,95%，BreakISO 18170.0%
Tensile stress change rate23°C,168hr,inDetergent(Tide),2.5%，BreakISO 18172.0%
Tensile stress change rate23°C,168hr,inCyclohexane，BreakISO 181720%
Tensile stress change rate23°C,168hr,inAceticAcid，BreakISO 1817-4.0%
Change rate of ultimate elongation in air125°C,168hr,inIRM903OilASTM D471-58%
Change rate of ultimate elongation in air125°C,70hr,inIRM903OilASTM D471-47%
Change rate of ultimate elongation in air100°C,168hr,inIRM903OilASTM D471-49%
Change rate of ultimate elongation in air100°C,168hr,inDeionizedWaterASTM D471-7.0%
Change rate of ultimate elongation in air23°C,168hr,inTrichloroethyleneASTM D47122%
Change rate of ultimate elongation in air23°C,168hr,inSulfuricAcid,98%ASTM D471-27%
Shore hardnessShoreA,100°C,168hr,inIRM903OilISO 1817-21
Shore hardnessShoreA,125°C,168hr,inIRM903OilISO 1817-23
Quality change rate23°C,168hr,inAceticAcidASTM D4714.0%
Quality change rate23.0°C,168hr,inSodiumChloride,15%ISO 18170.20%
Quality change rate23.0°C,168hr,inDetergent(Tide),2.5%ISO 18170.60%
Quality change rate23.0°C,168hr,inSulfuricAcid,98%ISO 18173.6%
Quality change rate100°C,168hr,inDeionizedWaterISO 18173.6%
Quality change rate23.0°C,168hr,inAceticAcidISO 18174.0%
Quality change rate100°C,168hr,inIRM903OilISO 181766%
Quality change rate125°C,168hr,inIRM903OilISO 181778%
Volume change125°C,70hr,在IRM903油中ASTM D47172%
Volume change125°C,70hr,在IRM903油中ISO 181772%
Shore hardnessShoreA,150°C,168hrISO 1887.0
Change rate of tensile strength in air23°C,168hr,inAceticAcidASTM D471-8.0%
Change rate of tensile strength in air23°C,168hr,inCyclohexaneASTM D47131%
Change rate of tensile strength in air23°C,168hr,inDetergent(Tide),2.5%ASTM D4713.0%
Change rate of tensile strength in air23°C,168hr,inEthanol,95%ASTM D471-2.0%
Change rate of tensile strength in air23°C,168hr,inHydrochloricAcid,10%ASTM D47113%
Change rate of tensile strength in air23°C,168hr,inIsopropylAlcoholASTM D47131%
Change rate of tensile strength in air23°C,168hr,inMethylethylketoneASTM D47147%
Tensile stress change rate23°C,168hr,inSodiumChloride,15%，BreakISO 1817-2.0%
Change rate of tensile strength in air23°C,168hr,inSodiumChloride,15%ASTM D4710.0%
Change rate of tensile strength in air23°C,168hr,inSodiumHydroxide,50%ASTM D4713.0%
Tensile stress change rate23°C,168hr,inHydrochloricAcid,10%，BreakISO 18179.0%
Tensile stress change rate23°C,168hr,inIsopropylAlcohol，BreakISO 181720%
Tensile stress change rate23°C,168hr,inMethylethylketone，BreakISO 181724%
Quality change rate23.0°C,168hr,inMethylethylketoneISO 1817-24%
Tensile stress change rate23°C,168hr,inSodiumHydroxide,50%，BreakISO 18172.0%
Tensile stress change rate23°C,168hr,inSulfuricAcid,98%，BreakISO 1817-27%
Tensile stress change rate23°C,168hr,inTrichloroethylene，BreakISO 181722%
Tensile stress change rate100°C,168hr,inDeionizedWater，BreakISO 1817-7.0%
Tensile stress change rate100°C,168hr,inIRM903Oil，BreakISO 1817-49%
Tensile stress change rate125°C,70hr,inIRM903Oil，BreakISO 1817-47%
Quality change rate23°C,168hr,inCyclohexaneASTM D471-4.9%
Quality change rate23°C,168hr,inDetergent(Tide),2.5%ASTM D4710.60%
Quality change rate23°C,168hr,inEthanol,95%ASTM D471-0.10%
Quality change rate23°C,168hr,inHydrochloricAcid,10%ASTM D4710.20%
Quality change rate23°C,168hr,inIsopropylAlcoholASTM D471-13%
Quality change rate23°C,168hr,inMethylethylketoneASTM D471-24%
Quality change rate23°C,168hr,inSodiumChloride,15%ASTM D4710.20%
Quality change rate23°C,168hr,inSodiumHydroxide,50%ASTM D471-0.20%
Quality change rate23°C,168hr,inSulfuricAcid,98%ASTM D4713.6%
Quality change rate23°C,168hr,inTrichloroethyleneASTM D471-6.0%
Quality change rate100°C,168hr,inDeionizedWaterASTM D4713.6%
Quality change rate100°C,168hr,inIRM903OilASTM D47166%
Quality change rate125°C,168hr,inIRM903OilASTM D47178%
Quality change rate23.0°C,168hr,inHydrochloricAcid,10%ISO 18170.20%
Quality change rate23.0°C,168hr,inIsopropylAlcoholISO 1817-13%
Quality change rate23.0°C,168hr,inTrichloroethyleneISO 1817-6.0%
Quality change rate23.0°C,168hr,inCyclohexaneISO 1817-4.9%
Quality change rate23.0°C,168hr,inSodiumHydroxide,50%ISO 1817-0.20%
Quality change rate23.0°C,168hr,inEthanol,95%ISO 1817-0.10%
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inAceticAcidASTM D471-2.0
Change rate of tensile strength in air23°C,168hr,inHydrochloricAcid,10%ISO 181713%
Change rate of tensile strength in air23°C,168hr,inIsopropylAlcoholISO 181731%
Change rate of tensile strength in air23°C,168hr,inMethylethylketoneISO 181747%
Change rate of tensile strength in air23°C,168hr,inSodiumChloride,15%ISO 18170.0%
Change rate of tensile strength in air23°C,168hr,inSodiumHydroxide,50%ISO 18173.0%
Change rate of tensile strength in air23°C,168hr,inSulfuricAcid,98%ISO 1817-17%
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inCyclohexaneASTM D471-16
Change rate of tensile strength in air23°C,168hr,inTrichloroethyleneISO 181754%
Change rate of tensile strength in air100°C,168hr,inDeionizedWaterISO 18171.0%
Change rate of tensile strength in air100°C,168hr,inIRM903OilISO 1817-30%
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inMethylethylketoneASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inSodiumChloride,15%ASTM D4710.0
Change rate of tensile strength in air125°C,70hr,inIRM903OilISO 1817-31%
Tensile stress change rate125°C,168hr,inIRM903Oil，BreakISO 1817-58%
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inDetergent(Tide),2.5%ASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inEthanol,95%ASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inHydrochloricAcid,10%ASTM D471-3.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inIsopropylAlcoholASTM D471-1.0
Change rate of tensile strength in air150°C,168hrISO 188-1.0%
Change rate of ultimate elongation in air150°C,168hrASTM D573-3.0%
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inSodiumHydroxide,50%ASTM D4710.0
Change rate of tensile strength in air150°C,168hrASTM D573-1.0%
Hardness change rate in the airShoreA,150°C,168hrASTM D5737.0
Change rate of tensile strength in air23°C,168hr,inSulfuricAcid,98%ASTM D471-17%
Change rate of tensile strength in air23°C,168hr,inTrichloroethyleneASTM D47154%
Change rate of tensile strength in air100°C,168hr,inDeionizedWaterASTM D4711.0%
Change rate of tensile strength in air100°C,168hr,inIRM903OilASTM D471-30%
Change rate of tensile strength in air125°C,70hr,inIRM903OilASTM D471-31%
Change rate of tensile strength in air125°C,168hr,inIRM903OilASTM D471-31%
Change rate of tensile strength in air23°C,168hr,inAceticAcidISO 1817-8.0%
Change rate of tensile strength in air23°C,168hr,inCyclohexaneISO 181731%
Change rate of tensile strength in air23°C,168hr,inDetergent(Tide),2.5%ISO 18173.0%
Change rate of tensile strength in air23°C,168hr,inEthanol,95%ISO 1817-2.0%
Change rate of tensile strength in air125°C,168hr,inIRM903OilISO 1817-31%
Change rate of ultimate elongation in air23°C,168hr,inAceticAcidASTM D471-4.0%
Change rate of ultimate elongation in air23°C,168hr,inCyclohexaneASTM D47120%
Change rate of ultimate elongation in air23°C,168hr,inDetergent(Tide),2.5%ASTM D4712.0%
Change rate of ultimate elongation in air23°C,168hr,inEthanol,95%ASTM D4710.0%
Change rate of ultimate elongation in air23°C,168hr,inHydrochloricAcid,10%ASTM D4719.0%
Change rate of ultimate elongation in air23°C,168hr,inIsopropylAlcoholASTM D47120%
Change rate of ultimate elongation in air23°C,168hr,inMethylethylketoneASTM D47124%
Change rate of ultimate elongation in air23°C,168hr,inSodiumChloride,15%ASTM D471-2.0%
Change rate of ultimate elongation in air23°C,168hr,inSodiumHydroxide,50%ASTM D4712.0%
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inSulfuricAcid,98%ASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inTrichloroethyleneASTM D471-3.0
Change rate of hardness (Shore) in the airShoreA,100°C,168hr,inDeionizedWaterASTM D471-2.0
Change rate of hardness (Shore) in the airShoreA,100°C,168hr,inIRM903OilASTM D471-21
Change rate of hardness (Shore) in the airShoreA,125°C,168hr,inIRM903OilASTM D471-23
Shore hardnessShoreA,23°C,168hr,inAceticAcidISO 1817-2.0
Shore hardnessShoreA,23°C,168hr,inCyclohexaneISO 1817-16
Shore hardnessShoreA,23°C,168hr,inDetergent(Tide),2.5%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inEthanol,95%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inHydrochloricAcid,10%ISO 1817-3.0
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Contact Us

Get App

Top