Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 25 g/10 min |
| Molten Volume Flow Rate (MVR) | | ISO 1133 | 21.0 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 1.9 % |
| Shrinkage rate | | ISO 294-4 | 1.9 % |
| Water absorption rate | | ISO 62 | 1.4 % |
| Water absorption rate | | ISO 62 | 0.30 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 92 |
| Rockwell hardness | | ISO 2039-2 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Limiting Oxygen Index | | ASTM D2863 | 23 % |
| atomization | | ISO 6452 | 95 % |
| atomization | | ISO 6452 | 2.0E-4 g |
| Emission | | VDA 275 | < 8.00 mg/kg |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 3300 Mpa |
| Tensile stress | | ISO 527-2 | 71.0 Mpa |
| Tensile strain | | ISO 527-2 | 12 % |
| Nominal tensile fracture strain | | ISO 527-2 | 23 % |
| Tensile creep modulus | | ISO 899-1 | 2800 Mpa |
| Tensile creep modulus | | ISO 899-1 | 1500 Mpa |
| Flexural modulus | | ISO 178 | 3000 Mpa |
| Poisson's ratio | | ISO 527 | 0.37 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 200 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 200 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 62631-3-2 | > 1.0E+15 ohms |
| Volume resistivity | | IEC 62631-3-1 | 1.0E+12 ohms·m |
| | IEC 62631-2-1 | 3.80 |
| | IEC 62631-2-1 | 3.80 |
| CTI | | IEC 60112 | 600 V |
| Hot wire ignition (HWI) | | UL 746 | 8.0 sec |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 到 4.0 hr |
| Suggested maximum moisture content | | | 0.20 % |
| Processing (melt) temperature | | | 210 到 220 °C |
| Melt Temperature, Optimum | | | 215 °C |
| Temperature | | | 80 到 100 °C |
| Mold Temperature, Optimum | | | 90 °C |
| pressure holding | | | 80.0 到 100 Mpa |
| pressure holding | | | yes |
| Hold Pressure Time | | | 8.00 s/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 162 °C |
| Heat distortion temperature | | ISO 75-2/A | 94.0 °C |
| vicat | | ISO 306/B50 | 160 °C |
| Melting temperature 2 | | ISO 11357-3 | 178 °C |
| | ASTM E831 | 1.0E-4 cm/cm/°C |
| | ISO 11359-2 | 1.2E-4 cm/cm/°C |
| | ISO 11359-2 | 1.2E-4 cm/cm/°C |
| Annealing Time - Optional | | | 30.0 min/mm |
| annealing temperature | | | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.