Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 2.0 g/10min |
| other | Test Condition | Test Method | Test Result |
|---|
| | | 低密度；高强度；可加工型良好 |
| colour | | | 清晰 透明 |
| purpose | | | 薄膜；层压板 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 0.921 g/cm |
| melt mass-flow rate | | ASTM D-1238 | 2 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D-638 | 850 % |
| Tensile strength at break | | ASTM D-638 | 250 kg/cm |
| bending strength | | ASTM D-747 | 2400 kg/cm |
| tensile strength | | ASTMD638 | 24.5 Mpa |
| elongation | | ASTMD638 | 800 % |
| | ASTMD747 | 270 Mpa |
| Flexural modulus | | ASTM D790/ISO 178 | 270(MPa) kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.923 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting point | | TPC法 | 123 °C |
| melting temperature | | | 122 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.