| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.15 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | DIN 53505 | 82 |
| ball-indentation hardness | | ISO 2039-1 | 165 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | Yield | ISO 527-2 | 70.0 MPa |
| Tensile strain | Break | ISO 527-2 | >50 % |
| Tensile modulus | | ISO 527-2 | 3300 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | >4.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 90.0 °C |
| melting temperature | | ISO 11357 | 213 °C |
| Linear coefficient of thermal expansion | | | 8E-05 cm/cm/°C |
| specific heat | | DIN 52612 | 1700 J/kg/°C |
| thermal conductivity | | DIN 52612 | 0.25 W/m/K |
| Usage temperature | | | -40-110 °C |
| Usage temperature | | | <160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.