Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | DIN53464 | 6E-03 % |
| Water absorption rate | | DIN53495 | 0.040 % |
| density | | DIN53479 | 1.08 g/cm³ |
| density | | DIN53479 | 1.08 g/cm³ |
| melt mass-flow rate | | DIN53735 | 5.0到8.0 g/10min |
| melt mass-flow rate | | DIN53735 | 5.0到8.0 g/10min |
| Shrinkage rate | | DIN53464 | 6E-03 % |
| Water absorption rate | | DIN53495 | 0.040 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ISO2039-2 | 88 |
| Rockwell hardness | R-Scale | ISO2039-2 | 88 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | Break | DIN53455 | 44.0 MPa |
| Tensile strain | Break | DIN53452 | 3.0 % |
| Flexural modulus | | DIN53457 | 3300 MPa |
| Bending stress | | DIN53457 | 70.0 MPa |
| Tensile stress | Break | DIN53455 | 44.0 MPa |
| Tensile strain | Break | DIN53452 | 3.0 % |
| Flexural modulus | | DIN53457 | 3300 MPa |
| Bending stress | | DIN53457 | 70.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | DIN53453 | 9.0 kJ/m² |
| Charpy Notched Impact Strength | | DIN53453 | 9.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+14 ohms |
| dielectric strength | | DIN53481 | 17 kV/mm |
| Surface Resistivity | | IEC60093 | 1E+14 ohms |
| dielectric strength | | DIN53481 | 17 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | DIN53461 | 120 °C |
| Melting Temperature | DIN53461 | 170 °C |
| Melting Temperature | DIN53461 | 170 °C |
| | DIN53461 | 135 °C |
| | DIN53461 | 135 °C |
| | DIN53461 | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.