PP BFI 300 Series
0
- Usages:Laminateuniversal
CompareTechnical Data Sheet
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | ASTMD2457 | 85 | |
| Haze ratio | ASTMD1003 | 2.5 % | |
| gloss | ASTMD2457 | 85 | |
| Haze ratio | ASTMD1003 | 2.5 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Sealing | 125 °C | ||
| 125 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD1894 | 0.18到0.25 | ||
| ASTMD1894 | 0.18到0.25 |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Falling hammer impact | ASTMD1709 | 150 g | |
| Elmondov tear strength | ASTMD1922 | 20 g | |
| ASTMD1922 | 90 g | ||
| Oxygen transmission rate | ASTMD3985 | 2800 cm³/m²/24hr | |
| Water vapor permeability | ASTME96 | 12 g/m²/24hr | |
| usage | 43.8 m²/kg | ||
| Secant modulus | ASTMD882 | 483 MPa | |
| ASTMD882 | 448 MPa | ||
| tensile strength | ASTMD882 | 44.8 MPa | |
| usage | 43.8 m²/kg | ||
| tensile strength | ASTMD882 | 37.9 MPa | |
| elongation | ASTMD882 | 650 % | |
| ASTMD882 | 700 % | ||
| Falling hammer impact | ASTMD1709 | 150 g | |
| Elmondov tear strength | ASTMD1922 | 20 g | |
| ASTMD1922 | 90 g | ||
| Oxygen transmission rate | ASTMD3985 | 2800 cm³/m²/24hr | |
| Water vapor permeability | ASTME96 | 12 g/m²/24hr | |
| Secant modulus | ASTMD882 | 483 MPa | |
| ASTMD882 | 448 MPa | ||
| tensile strength | ASTMD882 | 44.8 MPa | |
| ASTMD882 | 37.9 MPa | ||
| elongation | ASTMD882 | 650 % | |
| ASTMD882 | 700 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.