EAA 3003 STYRON US

Form：Granules | Grade：Extrusion grade

Properties:

Heat sealing performancehigh strengthHigh toughnessResistance to stress crac

Typical Applications:

chipcontainerFood packaging

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	chip \| container \| Food packaging
Properties:	Heat sealing performance \| high strength \| High toughness \| Resistance to stress crac

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Starting temperature of heat sealing		Internal Method		℃
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190℃/2.16kg	ASTM D-1238	7.8	g/10min
melt mass-flow rate	melt mass-flow rate	190℃/2.16kg	ISO 1133	7.8	g/10min
Monomer content		Internal Method		%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	2% Secant	ASTM D-638	130	MPa
Tensile modulus	Tensile modulus	2% Secant	ISO 527-2	130	MPa
tensile strength	Yield	ASTM D-638	7.5	MPa
	tensile strength	Yield	ISO 527-2	7.5	MPa
	tensile strength	tensile strength	Break	ASTM D-638	18	MPa
Tensile modulus	2%Secant	ASTMD638	130	Mpa
tensile strength	Yield	ASTMD638	7.50	Mpa
tensile strength	tensile strength	Break	ASTMD638	18.0	Mpa
elongation	Break	ASTMD638	590	%
tensile strength	Break	ISO 527-2	18	MPa
Elongation at Break		ASTM D-638	590	%
Elongation at Break	Elongation at Break		ISO 527-2	590	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		Internal Method		℃
Vicat softening temperature		ISO 306/A	90.0	°C
Melting temperature		Internal Method	100	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16kg	ASTMD1238	7.8	g/10min
Content of comonomer		Internal Method	6.5	%
film	Test Condition	Test Method	Test Result	Test Unit
Initial sealing temperature		Internal Method	90.0	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.