PC DX11355-BKNAT SABIC INNOVATIVE NANSHA

274

Form：Granules | Grade：Injection grade

Properties:

Thermal stabilityHigh mobility

Typical Applications:

Automotive componentsElectronic and electrical components

Supplier(8)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive components \| Electronic and electrical components
Properties:	Thermal stability \| High mobility

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23°C	ASTM D4812	2100	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.60mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Break, 50.0 mm Span		89	Mpa
bending strength	bending strength	Yield, 50.0 mm Span		90	Mpa
Bending modulus	50.0 mm Span	ASTM D790	2400	Mpa
elongation	Break		70	%
elongation	elongation	Yield		5.4	%
tensile strength	Break		52	Mpa
tensile strength	tensile strength	Yield		58	Mpa
Tensile modulus		ASTM D638	2600	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Suggested maximum moisture content			0.02	%
Suggested injection volume			30 to 80	%
Hopper temperature			60 to 80	°C
Temperature at the rear of the barrel			250 to 290	°C
Temperature in the middle of the barrel			255 to 295	°C
Temperature at the front of the material cylinder			260 to 300	°C
Spray nozzle temperature			275 to 300	°C
drying time			3.0 to 4.0	hr
drying temperature			100 to 110	°C
Screw speed			40 to 70	rpm
Exhaust hole depth			0.038 to 0.076	mm
Processing (melt) temperature			275 to 300	°C
Mold temperature			60 to 90	°C
Back pressure			0.300 to 0.700	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI		UL 746B	80	°C
RTI Imp		UL 746B	80	°C
RTI Elec		UL 746B	80	°C
Linear coefficient of thermal expansion	垂直 : -40 to 40°C		0.000067	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -40 to 40°C		0.000062	cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	114	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	24 hr, 23°C, 50% RH	ASTM D570	0.01	%
Shrinkage rate	Across FlowFlow : 24hr		0.5	%
Shrinkage rate	Shrinkage rate	Flow : 24hr		0.5	%
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	12	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1.00 GHz	IEC 60250	0.007
Relative permittivity	1.00 GHz	IEC 60250	2.92

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top