EVOH F101B NIPPON GOHSEI
651
- Properties:copolymerLubricity
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 1.6 | g/10min |
| 210°C/2.16kg | ISO1133 | 3.8 | g/10min | |
| Ethylene | 内部方法 | 32.0 | mol% |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M计秤 | ISO2039-2 | 100 | |
| Tensile modulus | ISO527-2 | 2700 | Mpa | |
| tensile strength | 断裂 | ISO527-2 | 34.0 | Mpa |
| elongation | 断裂 | ISO527-2 | 15 | % |
| Bending modulus | ISO178 | 3800 | Mpa | |
| Cantilever beam without notch impact strength | ISO180 | 2.9 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glass transition temperature | ISO11357-2 | 69.0 | °C | |
| vicat softening point | ISO306 | 173 | °C | |
| Melting temperature | ISO11357-3 | 183 | °C | |
| Crystallization peak temperature | ISO11357-3 | 161 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen permeability rate | 20°C,100%RH | ISO14663-2 | 0.38 | cm³·mm/m²/atm/24hr |
| 20°C,35%RH | ISO14663-2 | 6E-03 | cm³·mm/m²/atm/24hr | |
| 20°C,65%RH | ISO14663-2 | 8E-03 | cm³·mm/m²/atm/24hr | |
| 20°C,85%RH | ISO14663-2 | 0.030 | cm³·mm/m²/atm/24hr | |
| 20°C,90%RH | ISO14663-2 | 0.060 | cm³·mm/m²/atm/24hr | |
| Water vapor permeability | ASTME96 | 1.6 | g·mm/m²/atm/24hr | |
| Oxygen permeability rate | 20°C,0%RH | ISO14663-2 | 4E-03 | cm³·mm/m²/atm/24hr |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.