Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO1133 | 0.11 g/10min |
| Resistance to environmental stress cracking | | ASTMD1693 | >600 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 62 |
| other | Test Condition | Test Method | Test Result |
|---|
| | | 抗化学性、耐应力开裂性、蠕变特性 |
| purpose | | | 普通配水管、电线铺设管、输水/ 下水管 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 0.11 g/10min |
| density | | ISO 1183 | 951 kg/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| yield point stress | | ISO 527-2 | 23 Mpa |
| elongation | | ISO 527-2 | ＞500 % |
| Tensile elasticity coefficient | | ISO 527-1 | 1000 Mpa |
| Flexural modulus | | ISO 178 | 1100 Mpa |
| pendulum impact strength | | ISO 179-1 | 17 KJ/m |
| D-type Shore hardness | | ISO 868 | 62 |
| Environmental stress cracking resistance | | ASTM D-1693 | ＞600 hours |
| Tensile modulus | | ISO527-2 | 1000 Mpa |
| Tensile stress | | ISO527-2 | 23.0 Mpa |
| Tensile strain | | ISO527-2 | >500 % |
| Flexural modulus | | ISO178 | 1100 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 17 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792/ISO 1183 | 0.9 |
| melt mass-flow rate | | ASTM D1238/ISO 1133 | 20 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306 | 122 °C |
| | ISO 11357-3 | 131 °C |
| vicat | | ISO306 | 122 °C |
| melting temperature | | ISO11357-3 | 131 °C |
| | ASTM D648/ISO 75 | 120 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.