PBT LNP™ THERMOCOMP™ WF1004 SABIC INNOVATIVE US
67
- Properties:Aging resistanceHigh mobilityFiller: Glass fiber reinf20% filler by weight
- Usages:Electronic and electrical components
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.30-0.50 % | |
| ASTM D955 | 1.0-3.0 % | ||
| Water absorption rate | ASTM D570 | 0.058 % | |
| ISO 62 | 0.073 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 117 Mpa | |
| ISO 527-2/5 | 114 Mpa | ||
| Tensile strain | ISO 527-2/5 | 2.5 % | |
| elongation | ASTM D638 | 2.8 % | |
| Tensile strain | ISO 527-2/5 | 2.5 % | |
| Flexural modulus | ASTM D790 | 7110 Mpa | |
| ISO 178 | 6660 Mpa | ||
| bending strength | ISO 178 | 173 Mpa | |
| ASTM D790 | 183 Mpa | ||
| ASTM D790 | 182 Mpa | ||
| Tensile modulus | ASTM D638 | 7580 Mpa | |
| ISO 527-2/1 | 7590 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO 180/1A | 6.1 kJ/m² | |
| Suspended wall beam without notch impact strength | ISO 180/1U | 35 kJ/m² | |
| Dart impact | ASTM D3763 | 7.10 J | |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 1.90 J |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 222 °C | |
| ISO 75-2/Bf | 218 °C | ||
| ASTM D648 | 207 °C | ||
| ISO 75-2/Af | 198 °C | ||
| Linear coefficient of thermal expansion | ASTM D696 | 3.9E-05 cm/cm/°C | |
| ASTM D696 | 1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.