PEEK 450FE20 VICTREX UK

Form：Granules | Grade：Enhanced level

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt viscosity	400°C	ISO 11443	350	Pa·s
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180	无断裂
Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Compressive stress	120°C	ISO 604	65.0	Mpa
Compressive stress	Compressive stress	23°C	ISO 604	105	Mpa
bending strength	275°C	ISO 178	13.0	Mpa
	bending strength	175°C	ISO 178	18.0	Mpa
		bending strength	125°C	ISO 178	70.0	Mpa
			bending strength	3.5%Strain,23°C	ISO 178	100	Mpa
			bending strength	bending strength	23°C6	ISO 178	125	Mpa
Bending modulus	23°C	ISO 178	3200	Mpa
Tensile strain	Break,23°C	ISO 527-2	25	%
tensile strength	Yield,23°C	ISO 527-2	78.0	Mpa
Tensile modulus	23°C	ISO 527-2	3200	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD:>143°C	ISO 11359-2	1.4E-04	cm/cm/°C
	Linear coefficient of thermal expansion	TD:<143°C	ISO 11359-2	6E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD:>143°C	ISO 11359-2	1.2E-04	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:<143°C	ISO 11359-2	4E-05	cm/cm/°C
Melting temperature		ISO 11357-3	343	°C
Glass transition temperature	--8	ISO 11357-2	150	°C
Glass transition temperature	Glass transition temperature	--7	ISO 11357-2	143	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	150	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD	ISO 294-4	1.2	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	1.7	%
Spiral flow length		Internal Method	13.0	CM
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	23°C	IEC 60093	1E+16	ohms·cm
Dielectric strength	2.00mm	IEC 60243-1	26	KV/mm
Dielectric constant	23°C,1kHz	IEC 60250	2.80
Dissipation factor	23°C,1MHz	IEC 60250	4E-03
Compared to the anti leakage trace index		IEC 60112	PLC 4
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	ShoreD,23°C	ISO 868	81

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.