Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792 | 1.04 g/cm³ |
Water absorption rate | Saturation | ASTM D570 | 0.060 % |
density | | ASTM D792 | 1.04 g/cm³ |
Water absorption rate | Saturation | ASTM D570 | 0.060 % |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | V-0 |
Limiting Oxygen Index | | ASTM D2863 | 29 % |
UL flame retardant rating | | UL 94 | V-0 |
Limiting Oxygen Index | | ASTM D2863 | 29 % |
film | Test Condition | Test Method | Test Result |
---|
handle | | ASTM D2578 | >50 dyne/cm |
tensile strength | | ASTM D882 | 22.1 MPa |
handle | | ASTM D2578 | >50 dyne/cm |
film thickness | | | 1500to1700 µm |
tensile strength | | ASTM D882 | 30.3 MPa |
film thickness | | | 1500to1700 µm |
tensile strength | | ASTM D882 | 30.3 MPa |
tensile strength | | ASTM D882 | 22.1 MPa |
Electrical performance | Test Condition | Test Method | Test Result |
---|
High arc combustion index (HAI) | | UL 746 | PLC 0 |
High Voltage Arc Traceability Rate (HVTR) | | UL 746 | mm/min |
Hot wire ignition (HWI) | | UL 746 | PLC 4 sec |
dielectric strength | | ASTM D149 | 45300 V |
Volume resistivity | | ASTM D257 | 4E+15 ohms·cm |
dielectric strength | | ASTM D149 | 29 kV/mm |
dielectric constant | | ASTM D150 | 2.30 |
Dissipation Factor | | ASTM D150 | 1.9E-03 |
Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 0 |
Volume resistivity | | ASTM D257 | 4E+15 ohms·cm |
dielectric strength | | ASTM D149 | 29 kV/mm |
dielectric constant | | ASTM D150 | 2.30 |
Dissipation Factor | | ASTM D150 | 1.9E-03 |
Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 0 |
High arc combustion index (HAI) | | UL 746 | PLC 0 |
High Voltage Arc Traceability Rate (HVTR) | | UL 746 | mm/min |
Hot wire ignition (HWI) | | UL 746 | PLC 4 sec |
dielectric strength | | ASTM D149 | 45300 V |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Hot deformation temperature (HDT) | | ASTM D648 | 121 °C |
RTI Elec | | UL 746 | 115 °C |
Hot deformation temperature (HDT) | | ASTM D648 | 121 °C |
RTI Elec | | UL 746 | 115 °C |
RTI | | UL 746 | 115 °C |
RTI | | UL 746 | 115 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.