PEEK 550GL30 JILIN JOINATURE

Form：Granules | Grade：Injection grade

Properties:

enhanceModerate liquidityGlass fiber reinforced

Typical Applications:

AerospaceElectrical fieldElectronic fieldElectric wireCableIndustrial machineryMedical suppliesNursing suppliesAutomotive sector

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Aerospace \| Electrical field \| Electronic field \| Electric wire \| Cable \| Industrial machinery \| Medical supplies \| Nursing supplies \| Automotive sector
Properties:	enhance \| Moderate liquidity \| Glass fiber reinforced

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength		ISO 179/1eA	8	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1U	55	kJ/m²
Impact strength of cantilever beam gap	有Notched	ISO 180-A	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/U	60	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	23℃	ISO 868	88	D 级
tensile strength	Break，23℃	ISO 527	175	Mpa
Tensile strain	Break，23℃	ISO 527	2.7	%
bending strength	Break，23℃	ISO 178	265	Mpa
Bending modulus	23℃	ISO 178	11300	Mpa
compressive strength	23℃	ISO 604	250	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 11357	343	°C
Hot deformation temperature	1.8 Mpa	ISO 75-f	328	°C
Glass transition temperature	起始	ISO 11357	143	°C
specific heat	23℃	DSC	1.7	kJ/kg/℃
Linear coefficient of thermal expansion	低于Tg沿着Flow	ISO 11359	18	ppm/K
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	高于Tg沿着Flow	ISO 11359	18	ppm/K
thermal conductivity	23℃	ISO 22007-4	0.3	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	结晶	ISO 1183	1.51	g/cm³
Water absorption rate	23℃，24hr，3.2 mm厚拉伸棒	ISO 62-1	0.04	%
Water absorption rate	Water absorption rate	Equilibrium，23℃，3.20 mm厚拉伸棒	ISO 62-1	0.3	%
Shrinkage rate	MD	ISO 294-4	0.8	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.3	%
melt mass-flow rate	380℃，5.0kg	ISO 1133	6	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	23 ℃，1V	IEC 60093	10^16	ohms·cm
Dielectric strength	2 mm	IEC 60243-1	25	KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 4
Dielectric constant	23 ℃, 1 kHz	IEC 60250	3.2
Dissipation factor	23℃, 1MHz，Tangent	IEC 60250	0.005

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.