ABS TAIRILAC® AG12A0 FCFC TAIWAN

2143

Properties:
High impact resistance
High impact resistance
General molding
Usages:
Footwear
Toy
Shell
Electrical enclosure
Plastic box
Plate
heel
Toy
Clock housing
Sound enclosure
suitcase
Certificates:
UL
FDA
MSDS
SGS
TDS
Processing
MSDS
UL
RoHS
SVHC
Environmental
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD	内部方法	0.40to0.70	%
Melt mass flow rate	200°C/5.0kg	ASTMD1238	1.6	g/10min
	Melt mass flow rate	220°C/10.0kg	ASTMD1238	16	g/10min
		Melt mass flow rate	200°C/5.0kg	ISO1133	1.6	g/10min
		Melt mass flow rate	Melt mass flow rate	220°C/10.0kg	ISO1133	16	g/10min
density		ASTMD792	1.04	g/cm³
density	density	23°C	ISO1183	1.04	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Impact strength of cantilever beam gap	23°C,6.35mm	ISO180	290	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,6.35mm	ASTMD256	290	J/m
tensile strength	23°C	ASTMD638	45.1	Mpa
tensile strength	tensile strength	屈服,23°C	ISO527-2	45.0	Mpa
Bending modulus	23°C	ASTMD790	2450	Mpa
Bending modulus	Bending modulus	23°C	ISO178	2450	Mpa
bending strength	23°C	ASTMD790	73.5	Mpa
bending strength	bending strength	23°C	ISO178	74.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
vicat softening point		ASTMD15253	102	°C
vicat softening point	vicat softening point		ISO306/A	102	°C
Hot deformation temperature	1.8MPa,未退火,12.7mm	ASTMD648	85.0	°C
	Hot deformation temperature	1.8MPa,Unannealed,12.7mm	ISO75-2/A	85.0	°C
		Hot deformation temperature	1.8MPa,Annealed	ASTMD648	95.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,退火	ISO75-2/A	95.0	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.