PP J705UG PRIME POLYMER JAPAN

Form：Granules | Grade：Wear resistant grade

Properties:

High rigidityAntistaticHigh impact resistance

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

High rigidity | Antistatic | High impact resistance

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			注塑高抗冲. 抗静电. 高刚性
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-20°C	ISO 179	4.0	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	10	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	1450	Mpa
tensile strength	Yield	ISO 527-2	29.0	Mpa
Tensile strain	Break	ISO 527-2	50	%
Tensile modulus		ISO 527-2	1450	Mpa
Tensile stress	Yield	ISO 527-2	29	Mpa
Tensile strain	Break	ISO 527-2	50	%
Charpy Notched Impact Strength	-20℃	ISO 179	4.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179	10	kJ/m²
Rockwell hardness		ISO 2039-2	95
Impact strength of cantilever beam gap		ASTM D256/ISO 179	10	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	50	%
Tensile modulus		ASTM D638/ISO 527	1450	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	29	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	95
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	105	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	105	°C
	Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	105	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/2.16kg	ISO 1133	9.0	g/10min
melt mass-flow rate	melt mass-flow rate	230℃,2.16kg	ISO 1133	9.0	g/10min
density		ASTM D792/ISO 1183	0.91
melt mass-flow rate		ASTM D1238/ISO 1133	9.0	g/10min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ISO 2039-2	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.