Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| MeltViscosity | | ISO11443-A | 210 Pa·s |
| Melt volume flow rate | | ISO1133 | 25.0 cm³/10min |
| Shrinkage rate | | ISO2577 | 0.55to0.75 % |
| Shrinkage rate | | ISO2577 | 0.55to0.75 % |
| Water absorption rate | | ISO62 | 0.70 % |
| Water absorption rate | | ISO62 | 0.20 % |
| density | | ISO1183 | 1.14 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| FlameRating | | UL94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/A | 15 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/A | 48 kJ/m² |
| | ISO180 | NoBreak |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2/50 | 53.0 MPa |
| Tensile strain | | ISO527-2/50 | 4.9 % |
| Tensile strain | | ISO527-2/50 | >50 % |
| Tensile modulus | | ISO527-2/1 | 2500 MPa |
| Tensile stress | | ISO527-2/50 | 62.0 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| | IEC60250 | 2.90 |
| Dissipation Factor | | IEC60250 | 3E-03 |
| Dissipation Factor | | IEC60250 | 9E-03 |
| CTI | | IEC60112 | 250 V |
| Surface Resistivity | | IEC60093 | 1E+17 ohms |
| Volume resistivity | | IEC60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC60243-1 | 35 kV/mm |
| | IEC60250 | 2.90 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 127 °C |
| | ISO75-2/A | 109 °C |
| vicat | | ISO306/B50 | 129 °C |
| vicat | | ISO306/B120 | 131 °C |
| | ISO11359-2 | 7E-05 cm/cm/°C |
| | ISO11359-2 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.