PC LEXAN™ ML7647-BK1D0080 SABIC EU
58
- Properties:High impact resistanceFatigue resistanceMiddle flow
- Usages:Fitness equipmentHousehold appliancesElectronic fieldElectrical field
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 12 g/10 min | |
| Melt volume flow rate | ISO 1133 | 11.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.50 - 0.80 % | |
| Water absorption rate | ISO 62 | 0.26 % | |
| ISO 62 | 0.15 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2180 Mpa | |
| ISO 527-2/1 | 2150 Mpa | ||
| tensile strength | ASTM D638 | 52.0 Mpa | |
| ISO 527-2/50 | 52.0 Mpa | ||
| ASTM D638 | 54.0 Mpa | ||
| ISO 527-2/50 | 50.0 Mpa | ||
| elongation | ASTM D638 | 5.0 % | |
| ISO 527-2/50 | 5.3 % | ||
| ASTM D638 | 100 % | ||
| ISO 527-2/50 | 94 % | ||
| Flexural modulus | ASTM D790 | 2130 Mpa | |
| ISO 178 | 2160 Mpa | ||
| bending strength | ISO 178 | 86.0 Mpa | |
| ASTM D790 | 87.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ASTM D3763 | 69.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 270 to 295 °C | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the front of the material cylinder | 295 to 315 °C | ||
| Spray nozzle temperature | 290 to 310 °C | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| Temperature | 70 to 95 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 118 °C | |
| ISO 75-2/Af | 119 °C | ||
| vicat | ASTM D15259 | 138 °C | |
| Linear coefficient of thermal expansion | ASTM E831 | 6.9E-5 cm/cm/°C | |
| ISO 11359-2 | 7.1E-5 cm/cm/°C | ||
| ASTM E831 | 7.2E-5 cm/cm/°C | ||
| ISO 11359-2 | 7.5E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.