PC/ABS 920MG TRINSEO NETHERLANDS

Form：Granules

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23℃23℃	ISO 179/1eU 2	No Break
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃-30℃	ISO 179/1eU 2	No Break
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-1-2	2250	Mpa
Tensile modulus	Tensile modulus		ISO 527-2 2	2050	Mpa
tensile strength	YieldYield	ISO 527-2 2	48	Mpa
tensile strength	tensile strength	YieldYield	ISO 527-2/50	50	Mpa
Tensile strain	BreakBreak	ISO 527-2/50	100	%
Tensile strain	Tensile strain	YieldYield	ISO 527-2 2	4.6	%
Nominal fracture strain		ISO 527-2 2	> 50	%
Bending modulus		ISO 178	2100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa，Unannealed1.8 MPa，Unannealed	ISO 75-2/A	105	°C
	Hot deformation temperature	1.8 MPa1.8 MPa	ISO 75-2 2	102	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa0.45 MPa	ISO 75-2 2	126	°C
Vicat softening temperature	B50B50	ISO 306	122	°C
Vicat softening temperature	Vicat softening temperature	B505.1kg，50℃/h	ISO 306 2	128	°C
Linear coefficient of thermal expansion	MD：-30~80℃MD：-30 to 80℃	ISO 11359-2	0.000073	1/℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183/B	1.12	g/cm³
density	density		ISO 1183-2	1.13	g/cm³
Apparent density		ISO 60	0.65	g/cm³
melt mass-flow rate	260℃，5.0kg260℃/5.0 kg	ISO 1133	17	g/10min
Melt Volume Flow Rate (MVR)	260℃，5 kg260℃/5.0 kg	ISO 1133	15	cm3/10min
Spiral flow length			51	CM
Shrinkage rate		ISO 294-4	0.35 - 0.45	%
Water absorption rate	SaturationSaturation	ISO 62-2	0.03	%
Water absorption rate	Water absorption rate	EquilibriumEquilibrium	ISO 62-2	0.28	%
Volatile compounds		VDA 277	9	µg/g
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.60 mm	ISO 1210 2	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.