physical property | Test Condition | Test Method | Test Result |
---|
density | | ISO 1183 | 1.42 g/cm³ |
melt mass-flow rate | | ISO 1133 | 7.0 g/10min |
flammability | Test Condition | Test Method | Test Result |
---|
burning rate | | ISO 3795 | <100 mm/min |
UL flame retardant rating | | UL 94 | HB |
UL flame retardant rating | | UL 94 | HB |
UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
UL flame retardant rating | | IEC 60695-11-10,-20 | HB |
FMVSS flammability | | FMVSS302 | B |
Fogging-G-value | | ISO 6452 | 4E-04 g |
Supplementary Information | Test Condition | Test Method | Test Result |
---|
Emission | | VDA275 | <8.00 mg/kg |
Emissions of Organic Compounds | | VDA277 | 7.30 µgC/g |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Charpy Notched Impact Strength | | ISO 179/1eA | 8.0 kJ/m² |
Charpy Notched Impact Strength | | ISO 179/1eA | 9.0 kJ/m² |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ISO 527-2 | 3300 Mpa |
tensile strength | | ISO 527-2 | 75.0 Mpa |
Tensile strain | | ISO 527-2 | 15 % |
Nominal tensile fracture strain | | ISO 527-2 | 28 % |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ISO 75-2/A | 103 °C |
melting temperature | | ISO 11357-3 | 178 °C |
AnnealingTemperature | | | 160 °C |
AnnealingTime-Optional | | | 30.0 min/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.