Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Shrinkage rate | | 内部方法 | 1.2 % |
Shrinkage rate | | 内部方法 | 1.2 % |
Water absorption rate | | 内部方法 | 2.5 % |
other | Test Condition | Test Method | Test Result |
---|
characteristic | | | 超高粘度 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ASTM D638/ISO 527 | 750屈服 >720断裂 kg/cm²(MPa)[Lb/in²] |
elongation | | ASTM D638/ISO 527 | 8 % |
Rockwell hardness | | ASTM D785 | 120 |
bending strength | | ASTM D790/ISO 178 | 400 kg/cm²(MPa)[Lb/in²] |
elongation at break | | ASTM D638/ISO 527 | >200 % |
Tensile modulus | | ISO 527-2 | 2800 Mpa |
tensile strength | | ISO 527-2 | 80.0 Mpa |
Tensile strain | | ISO 527-2 | >50 % |
Flexural modulus | | ISO 178 | 2700 Mpa |
bending strength | | ISO 178 | 110 Mpa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Impact strength of simply supported beam without notch | | ISO 179 | 5.0 kJ/m² |
Physical properties | Test Condition | Test Method | Test Result |
---|
density | | ASTM D792/ISO 1183 | 1.14 |
Shrinkage rate | | ASTM D955 | 1.3 % |
Water absorption rate | | ASTM D570/ISO 62 | 1.8 % |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Volume resistivity | | ASTM D257/IEC 60093 | 1X10^15 Ω.cm |
relative permittivity | | IEC 60250 | 3.50 |
Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 0 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Linear coefficient of thermal expansion | | ASTM D696/ISO 11359 | 8 mm/mm.℃ |
Heat distortion temperature | | ISO 75-2/A | 60.0 °C |
Linear coefficient of thermal expansion | | ISO 11359-2 | 8E-05 cm/cm/°C |
Heat distortion temperature | | ISO 75-2/B | 145 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.