PEI ProPolymers PEI 2300
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTMD955 | 0.20到0.40 % | |
| Water absorption rate | ASTMD570 | 0.16 % | |
| density | ASTMD792 | 1.51 g/cm³ | |
| melt mass-flow rate | ASTMD1238 | 5.0 g/10min | |
| Shrinkage rate | ASTMD955 | 0.20到0.40 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M-Scale | 114 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTMD638 | 169 MPa |
| elongation | Break | ASTMD638 | 2.5 % |
| Flexural modulus | ASTMD790 | 8960 MPa | |
| bending strength | ASTMD790 | 228 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTMD256 | 80 J/m | |
| ASTMD256 | 10.0 kJ/m² | ||
| Suspended wall beam without notch impact strength | ASTMD256 | 430 J/m | |
| ASTMD256 | 40.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTMD1525 | 228 °C | |
| Heat Deflection Temperature | ASTMD648 | 212 °C | |
| ASTMD648 | 210 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.