LCP E130I VC3052 CELANESE USA

Form：Granules | Grade：Extrusion grade

Properties:

heat-resistingFlame retardantenhance

Typical Applications:

Household appliancesHousehold appliances

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Household appliances \| Household appliances
Properties:	heat-resisting \| Flame retardant \| enhance

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	31	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	43	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	V-0
Extreme Oxygen Index		ISO 4589-2	45	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Fracture bending strain		ISO 178	2.2	%
CompressiveStress	1%Strain	ISO 604	93.0	Mpa
Compressive modulus		ISO 604	14000	Mpa
bending strength	23°C	ISO 178	220	Mpa
Bending modulus	23°C	ISO 178	13500	Mpa
Tensile modulus		ISO 527-2/1A/1	15000	Mpa
tensile strength	Break	ISO 527-2/1A/5	150	Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.6	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-06	cm/cm/°C
Melting temperature		ISO 11357-3	335	°C
Vicat softening temperature		ISO 306/B50	195	°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	216	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	276	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	ISO 294-4	0.40	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	0.10	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.030	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112		V
Arc resistance		Internal Method	140	sec
Dissipation factor	2.05GHz	Internal Method	6E-03
	Dissipation factor	1MHz	IEC 60250	0.025
	Dissipation factor	Dissipation factor	100Hz	IEC 60250	0.010
Dielectric strength		IEC 60243-1	32	KV/mm
Volume resistivity		IEC 60093	1E+15	ohms·cm
Surface resistivity		IEC 60093	1E+14	ohms
Relative permittivity	2.05GHz	Internal Method	4.23
	Relative permittivity	1MHz	IEC 60250	3.30
	Relative permittivity	Relative permittivity	100Hz	IEC 60250	4.00
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	71

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.