Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO1133 | 8.00 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.50to0.70 % |
| Shrinkage rate | | 内部方法 | 0.50to0.70 % |
| Water absorption rate | | ISO62 | 0.20 % |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | ASTMD1003 | 52.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 875 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 875 °C |
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-2 |
| Burning wire flammability index | | IEC60695-2-12 | 850 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2/50 | 61.0 Mpa |
| Tensile modulus | | ISO527-2/1 | 2400 Mpa |
| Tensile stress | | ISO527-2/50 | 54.0 Mpa |
| Tensile strain | | ISO527-2/50 | 6.0 % |
| Nominal tensile fracture strain | | ISO527-2/50 | >50 % |
| Bending modulus 2 | | ISO178 | 2100 Mpa |
| Bending stress 2 | | ISO178 | 93.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | NoBreak |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 129 °C |
| | ISO11359-2 | 7E-05 cm/cm/°C |
| | ISO11359-2 | 7E-05 cm/cm/°C |
| RTI Elec | | UL746 | 125 °C |
| RTI Imp | | UL746 | 115 °C |
| RTI Str | | UL746 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.