Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.48 g/cm³ |
| Apparent density | | ASTMD1895 | 0.71 g/cm³ |
| Shrinkage rate | | ASTMD955 | 0.83 % |
| Water absorption rate | | ASTMD570 | 0.27 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTMD785 | 79 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-1 |
| Limiting Oxygen Index | | ASTMD2863 | 29 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| compressive strength | | ASTMD695 | 176 MPa |
| Tensile modulus | | ASTMD638 | 9120 MPa |
| tensile strength | | ASTMD638 | 57.0 MPa |
| elongation | Break | ASTMD638 | 0.80 % |
| Flexural modulus | | ASTMD790 | 8030 MPa |
| bending strength | | ASTMD790 | 89.1 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ASTMD256 | 16.5 J/m |
| Impact strength of cantilever beam gap | | ASTMD256 | 15 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 4.1E+11 ohms·cm |
| dielectric strength | | ASTMD149 | 11 kV/mm |
| dielectric strength | | ASTMD149 | 7.7 kV/mm |
| dielectric constant | | ASTMD150 | 5.20 |
| Dissipation Factor | | ASTMD150 | 0.060 |
| arc resistance | | ASTMD495 | 158 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | 175 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 167 °C |
| Continuous use temperature | | ASTMD794 | 206 °C |
| | ASTME831 | 5E-05 cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.49 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.