PA6 B30S LANXESS BELGIUM

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Alternative Model(4)

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23℃23 °C	ISO 179-1eA	<10	kJ/m²
	Charpy Notched Impact Strength	-30℃-30 °C	ISO 179-1eA	<10	kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃23 °C	ISO 179-1eU	N	kJ/m²
Impact strength of cantilever beam gap	23℃23 °C	ISO 180-1A	<10
	Impact strength of cantilever beam gap	-30℃-30 °C	ISO 180-1A	<10
		Impact strength of cantilever beam gap	23℃23 °C	ISO 180-1U	N	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃-30 °C	ISO 180-1U	200	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	1 mm/min1 mm/min	ISO 527-1	3200	Mpa
Tensile stress	50 mm/min50 mm/min，Yield	ISO 527-1	80	Mpa
Bending modulus	2 mm/mim2 mm/min	ISO 178	2800	Mpa
bending strength	2 mm/min2 mm/min	ISO 178	105	Mpa
Bending strain	2 mm/min2 mm/min	ISO 178	6	%
bending strength	3.50% Strain，2 mm/min3.5%，2 mm/min	ISO 178	90	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature	10℃ / min10 ℃/min	ISO 11357-1	221	°C
Hot deformation temperature	1.8 MPa1.80 MPa	ISO 75-1/2	66	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa0.45 MPa	ISO 75-1/2	172	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1122	g/cm³
Shrinkage rate	MD：60x60x2，270℃ / WZ 80℃，600 bar平行,60x60x2; 270 °C / WZ 80 °C; 600 bar	ISO 2577	1.03	%
	Shrinkage rate	正常，60x60x2，270℃ / WZ 80℃，600 bar正常,60x60x2; 270 °C / WZ 80 °C; 600 bar	ISO 2577	0.91	%
		Shrinkage rate	平行，60x60x2; 120 ℃; 4 h平行,60x60x2; 120 °C; 4 h	ISO 2577	0.27	%
		Shrinkage rate	Shrinkage rate	正常，60x60x2; 120 ℃; 4 h正常,60x60x2; 120 °C; 4 h	ISO 2577	0.27	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.