'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA66 9A22125 H 4Plas
Properties:
Filler reinforcement material glass fiber reinforcement material 25% filler additive by weight thermal stabilizer characteristics thermal stability
Product Description
Certificates(0)
Datasheet
Product Description
| Properties: | Filler | reinforcement material | glass fiber reinforcement material | 25% | filler additive by weight | thermal stabilizer characteristics | thermal stability |
Certificates
No Data...
Technical Data Sheet
| other | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Burning wire flammability index | 2.00 mm | IEC 60695-2-12 | 650 | °C |
| UL flame retardant rating | 3.20 mm | UL 94 | HB | |
| 1.60 mm | UL 94 | HB | ||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 65 | kJ/m² |
| -30°C | ISO 180/1U | 60 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 | kJ/m² |
| 23°C | ISO 180/1A | 8.0 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.6mm | UL 94 | HB | |
| 3.2mm | UL 94 | HB | ||
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 | °C |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | 23°C | ISO 527-2/5 | 8500 | MPa |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 65 | kJ/m² |
| -30°C | ISO 180/1U | 60 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 | kJ/m² |
| -30°C | ISO 180/1A | 7.0 | kJ/m² | |
| Tensile strain | Break, 23°C | ISO 527-2/5 | 3.0 | % |
| tensile strength | Break, 23°C | ISO 527-2/5 | 170.0 | MPa |
| Tensile modulus | 23°C | ISO 527-2/5 | 8500 | MPa |
| tensile strength | Break,23°C | ISO 527-2/5 | 170 | MPa |
| Tensile strain | Break,23°C | ISO 527-2/5 | 3.0 | % |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Melting temperature | ISO 11357 | 262 | °C | |
| Vicat softening temperature | ISO 306/B | 255 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 255 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 260 | °C | |
| Melting temperature | ISO 11357 | 262 | °C | |
| Vicat softening temperature | ISO 306/B | 255 | °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 255 | °C |
| 0.45 MPa, Unannealed | ISO 75-2/B | 260 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ISO 1183 | 1.32 | g/cm³ | |
| Shrinkage rate | TD | 1.1 | % | |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 2.0 | % |
| density | ISO 1183 | 1.32 | g/cm³ | |
| Shrinkage rate | TD | 1.1 | % | |
| MD | 0.30 | % | ||
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 2.0 | % |
| water content | ISO 960 | <2000 | ppm | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | IEC 60093 | 1E+13 | ohms | |
| Compared to the anti leakage trace index | IEC 60112 | PLC 1 | ||
| Volume resistivity | IEC 60093 | 1E+15 | ohms·cm | |
| Surface resistivity | IEC 60093 | 1E+13 | ohms | |
| Compared to the anti leakage trace index | IEC 60112 | PLC 1 | ||
| Volume resistivity | IEC 60093 | 1E+15 | ohms·cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.