Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.30 g/cm³ |
| spiral flow length | | 内部方法 | 20.0 cm |
| Shrinkage rate | | ISO 294-4 | 1.2 % |
| Shrinkage rate | | ISO 294-4 | 1.0 % |
| Water absorption rate | | ISO 62 | 0.60 % |
| Water absorption rate | | ISO 62 | 0.75 % |
| MeltViscosity | | ISO 11443 | 200 Pa·s |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ISO 868 | 86 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 24 % |
| Limiting Oxygen Index | | ISO 4589-2 | 35 % |
| toxicity | | NES713 | 0.0740 |
| toxicity | | NES713 | 0.150 |
| toxicity | | NES713 | 0.220 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 4300 MPa |
| tensile strength | | ISO 527-2 | 115 MPa |
| Tensile strain | | ISO 527-2 | 25 % |
| bending strength | | ISO 178 | 180 MPa |
| bending strength | | ISO 178 | 105 MPa |
| bending strength | | ISO 178 | 32.0 MPa |
| bending strength | | ISO 178 | 16.0 MPa |
| compression stress | | ISO 604 | 140 MPa |
| compression stress | | ISO 604 | 90.0 MPa |
| compression stress | | ISO 604 | 30.0 MPa |
| Flexural modulus | | ISO 178 | 4000 MPa |
| bending strength | | ISO 178 | 130 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179 | NoBreak |
| Impact strength of cantilever beam gap | | ISO 180/A | 5.5 kJ/m² |
| Suspended wall beam without notch impact strength | | ISO 180 | NoBreak |
| Charpy Notched Impact Strength | | ISO 179/1eA | 3.8 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Volume resistivity | | IEC 60093 | 1E+09 ohms·cm |
| dielectric strength | | IEC 60243-1 | 23 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 4 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359-2 | 4.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| thermal conductivity | | ISO 22007-4 | 0.29 W/m/K |
| thermal conductivity | | ISO 22007-4 | 0.32 W/m/K |
| Heat distortion temperature | | ISO 75-2/Af | 163 °C |
| Glass Transition Temperature | | ISO 11357-2 | 152 °C |
| Glass Transition Temperature | | ISO 11357-2 | 160 °C |
| melting temperature | | ISO 11357-3 | 373 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.