TPV 4175N TEKNOR APEX BELGIUM

Form：Granules | Grade：Weather resistant grade

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.00 mm	UL 94	HB
elastomer	Test Condition	Test Method	Test Result	Test Unit
tensile strength	横向Flow : 100%Strain	ASTM D412	3.3	Mpa
	tensile strength	Flow : 100%Strain	ASTM D412	5.3	Mpa
		tensile strength	横向Flow : Break	ASTM D412	8.5	Mpa
		tensile strength	tensile strength	Flow : Break	ASTM D412	7.2	Mpa
elongation	横向Flow : Break	ASTM D412	590	%
elongation	elongation	Flow : Break	ASTM D412	300	%
tear strength	-Across Flow	ASTM D624	39	kN/m
tear strength	tear strength	--1，Across Flow	ISO 34-1	39	kN/m
Permanent compression deformation	23°C, 22 hr	ASTM D395	22	%
	Permanent compression deformation	70°C, 22 hr	ASTM D395	31	%
	Permanent compression deformation	Permanent compression deformation	125°C, 70 hr	ASTM D395	45	%
squeeze out	Test Condition	Test Method	Test Result	Test Unit
Temperature in Zone 1 of the material cylinder			180 to 200	°C
Temperature in Zone 2 of the material cylinder			180 to 205	°C
Temperature in Zone 3 of the material cylinder			187 to 210	°C
Temperature in Zone 4 of the material cylinder			187 to 210	°C
Melt Temperature			195 to 215	°C
Oral mold temperature			195 to 215	°C
Traction roller			20.0 to 50.0	°C
injection	Test Condition	Test Method	Test Result	Test Unit
Temperature at the rear of the barrel			180 to 215	°C
Temperature in the middle of the barrel			180 to 215	°C
Temperature at the front of the material cylinder			180 to 215	°C
Spray nozzle temperature			187 to 220	°C
Processing (melt) temperature			185 to 220	°C
Mold temperature			10.0 to 55.0	°C
Back pressure			0.100 to 1.00	Mpa
Screw speed			100 to 200	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Elec		UL 746	100	°C
RTI Imp		UL 746	65	°C
RTI		UL 746	100	°C
hardness	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	Shore A, 5 Sec, 挤塑	ASTM D2240	72
Shore hardness	Shore hardness	Shore A, 5 Sec, Injection	ASTM D2240	75
aging	Test Condition	Test Method	Test Result	Test Unit
Change rate of tensile strength in air	135°C, 1000 hr，Across Flow	ISO 188	-2	%
	Change rate of tensile strength in air	150°C, 168 hr，Across Flow	ISO 188	-9	%
		Change rate of tensile strength in air	100% Strain 150°C, 168 hr，Across Flow	ISO 188	3	%
		Change rate of tensile strength in air	Change rate of tensile strength in air	100% Strain 150°C, 1000 hr，Across Flow	2.45	5	%
Tensile stress variation during fracture in air - transverse flow rate	135°C, 1000 hr	2.45	-5	%
	Tensile stress variation during fracture in air - transverse flow rate	150°C, 168 hr	2.45	-16	%
Change rate of hardness (Shore) in the air	Shore A, 135°C, 1000 hr		2.45	2
Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	Shore A, 150°C, 168 hr		2.45	3
Volume change	125°C, 70 hr, 在 IRM 903 油中	ASTM D471	78	%
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Apparent Shear Viscosity - Capillary @ 206/s	200°C	ASTM D3835	340	Pa·s
Apparent Shear Viscosity - Capillary @ 206/s	Apparent Shear Viscosity - Capillary @ 206/s	200°C	ISO 11443	340	Pa·s

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.