PPS PPS-hGR30 SICHUAN DEYANG

Form：Granules | Grade：Injection grade

Properties:

enhance

Typical Applications:

AerospaceMechanical componentsElectrical appliancesElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Aerospace \| Mechanical components \| Electrical appliances \| Electronic field \| Electrical field
Properties:	enhance

Certificates

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		GB/T 1033-1986	1.55	g/cm³
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
compressive strength		GB/T 1041-1992	140	Mpa
Rockwell hardness		GB/T 9342-1988	100	hr
elongation	Break	GB/T 1040-1992	1.70	%
Bending modulus		GB/T 1042-1992	1.1×104	Mpa
bending strength		GB/T 1042-1992	180	Mpa
Impact strength of cantilever beam gap		GB/T 1843-1996	11.5	kJ/m²
tensile strength		GB/T 1040-1992	142	Mpa
Elongation at Break		ASTM D638/ISO 527	1.7	%
tensile strength		ASTM D638/ISO 527	142	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	100
Bending modulus		ASTM D790/ISO 178	1.1*100000	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	180	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		GB/T 4608-1984	282	°C
Hot deformation temperature	1.80MPa	GB/T 1634-1979(1989)	267	°C
Combustibility	垂直法	GB/T 2408-1996	FV-0	级
Melting temperature			282	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		GB/T 15585-1995	0.0025	mm/mm
density		ASTM D792/ISO 1183	1.55
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	1MHz	GB/T 1409-1988	4
Dielectric strength		GB/T 1408.1-1999	18.56	KV/mm
Surface resistivity		GB/T 1410-1989	2.3×1015	Ω
Volume resistivity		GB/T 1410-1989	1.0×1015	Ω.m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.