Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.17 g/cm³ |
| Melt volume flow rate | | ISO1133 | 40.0 cm³/10min |
| Shrinkage rate | | ISO294-4 | 0.50 % |
| Water absorption rate | | ISO62 | 0.60 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | IEC60695-11-10,-20 | V-0 |
| Flammability level | | IEC60695-11-10,-20 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 800 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 775 °C |
| Limiting Oxygen Index | | ISO4589-2 | 32 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | Yield | ISO527-2 | 4.0 % |
| Nominal tensile fracture strain | | ISO527-2 | >50 % |
| Flexural modulus | | ISO178 | 2800 MPa |
| Tensile modulus | | ISO527-2 | 2850 MPa |
| Tensile stress | Yield | ISO527-2 | 60.0 MPa |
| Bending stress | | ISO178 | 110 MPa |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| ThermalConductivityofMelt | | | 0.23 W/m/K |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | | ISO180/4A | 45 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 2 |
| CTI | | IEC60112 | 325 V |
| Surface Resistivity | | IEC60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC60093 | >1.0E+15 ohms·cm |
| | IEC60250 | 3.00 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 90.0 °C |
| vicat | | ISO306/B50 | 104 °C |
| BallPressure Test | | IEC60695-10-2 | Pass |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare