Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.14 g/cm³ |
| melt mass-flow rate | | ISO1133 | 0.90 g/10min |
| Water absorption rate | | ISO62 | 0.50 % |
| Water absorption rate | | ISO62 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO868 | 40 |
| | ISO868 | 37 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO3795 | <100 mm/min |
| FMVSS flammability | | FMVSS302 | B |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile stress | | ISO527-2 | 23.0 MPa |
| Tensile strain | Break | ISO527-2 | >300 % |
| Nominal tensile fracture strain | | ISO527-2 | 350 % |
| Flexural modulus | | ISO178 | 80.0 MPa |
| Tensile modulus | | ISO527-2 | 80.0 MPa |
| Tensile stress | Break | ISO527-2 | 28.0 MPa |
| Tensile stress | | ISO527-2 | 7.00 MPa |
| Tensile stress | | ISO527-2 | 12.0 MPa |
| Tensile stress | | ISO527-2 | 13.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | | ISO179/1eU | NoBreak |
| Impact strength of cantilever beam gap | | ISO180/1A | NoBreak |
| Tensile impact strength | | ISO8256/1 | 300 kJ/m² |
| Charpy Notched Impact Strength | | ISO179/1eA | NoBreak |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tear strength | Across Flow | ISO34-1 | 120 kN/m |
| tear strength | | ISO34-1 | 110 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 4E+14 ohms |
| Volume resistivity | | IEC60093 | 8E+12 ohms·cm |
| dielectric strength | | IEC60243-1 | 19 kV/mm |
| Dissipation Factor | | IEC60250 | 0.030 |
| Dissipation Factor | | IEC60250 | 9.5E-03 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| PeakCrystallizationTemperature | | ISO11357-3 | 167 °C |
| | ISO11359-2 | 1.7E-04 cm/cm/°C |
| | ISO11359-2 | 2.3E-04 cm/cm/°C |
| | ISO11359-2 | 2E-04 cm/cm/°C |
| | ISO11359-2 | 5.44E-08 m²/s |
| | ISO11359-2 | 2.4E-04 cm/cm/°C |
| Heat distortion temperature | | ISO75-2/B | 56.0 °C |
| Heat distortion temperature | | ISO75-2/A | 42.0 °C |
| brittle temperature | | ISO974 | -100 °C |
| Glass Transition Temperature | | ISO11357-2 | -70.0 °C |
| melting temperature | | ISO11357-3 | 207 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.