ULDPE 4404G STYRON US

Form：Granules | Grade：Thin film grade

Properties:

optical performance High toughnessHigh toughness and opticaCertified by Canadian HPF

Typical Applications:

chipfilmMainly used for packaging

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	chip \| film \| Mainly used for packaging
Properties:	optical performance \| High toughness \| High toughness and optica \| Certified by Canadian HPF

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transparency		ASTM D-1746	99
gloss	45°	ASTM D-2457	90
turbidity		ASTM D-1003	1.8	%
gloss	45°,20.3μm	ASTM D2457	92
gloss	gloss	45°,50.8μm	ASTM D2457	90
transparency	20.3μm	ASTM D1746	99.0
transparency	transparency	50.8μm	ASTM D1746	99.0
turbidity	20.3μm	ASTM D1003	0.60	%
turbidity	turbidity	50.8μm	ASTM D1003	1.8	%
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate		ASTM D1238	4	g/10min
density		ASTM D792	0.904	g/cm³
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Puncture intensity		陶氏企业测试	17	J/cm³
tensile strength	Yield,TD	ASTM D-882	5	Mpa
	tensile strength	Yield,MD	ASTM D-882	7	Mpa
		tensile strength	TD，Break	ASTM D-882	32	Mpa
		tensile strength	tensile strength	MD，Break	ASTM D-882	33	Mpa
Elongation at Break	TD	ASTM D-882	714	%
Elongation at Break	Elongation at Break	MD	ASTM D-882	664	%
Tensile modulus	TD，2% Secant	ASTM D-882	63	Mpa
Tensile modulus	Tensile modulus	MD，3% Secant	ASTM D-882	63	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ASTM D-1525	71	°C
Vicat softening temperature	Vicat softening temperature		ASTM D1525	71.1	°C
Melting temperature		Internal Method	124	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	190°C/2.16kg	ASTM D1238	4.0	g/10min
film	Test Condition	Test Method	Test Result	Test Unit
Dart impact	20μm	ASTM D1709B	>850	g
Dart impact	Dart impact	51μm	ASTM D1709B	>850	g
Elmendorf tear strength	MD:20μm	ASTM D1922	330	g
	Elmendorf tear strength	MD:51μm	ASTM D1922	960	g
		Elmendorf tear strength	TD:20μm	ASTM D1922	500	g
		Elmendorf tear strength	Elmendorf tear strength	TD:51μm	ASTM D1922	1100	g
Oxygen permeability	23°C,51μm	ASTM D3985	450	cm³·mm/m²/atm/24hr
Water vapor permeability	51μm	ASTMF1249	0.85	g·mm/m²/atm/24hr
Carbon dioxide transmittance	23°C,50.8μm	Internal Method	2000	cm³·mm/m²/atm/24hr
Thin film puncture strength	20μm	Internal Method	18.9	J/cm³
Thin film puncture strength	Thin film puncture strength	51μm	Internal Method	17.5	J/cm³
Secant modulus	2%Secant,MD:20μm	ASTM D882	58.8	Mpa
	Secant modulus	2%Secant,MD:51μm	ASTM D882	62.6	Mpa
		Secant modulus	2%Secant,TD:20μm	ASTM D882	64.7	Mpa
		Secant modulus	Secant modulus	2%Secant,TD:51μm	ASTM D882	63.0	Mpa
tensile strength	MD:Yield,20μm	ASTM D882	7.00	Mpa
	tensile strength	MD:Yield,51μm	ASTM D882	6.76	Mpa
		tensile strength	TD:Yield,20μm	ASTM D882	4.92	Mpa
			tensile strength	TD:Yield,51μm	ASTM D882	6.34	Mpa
				tensile strength	MD:Break,20μm	ASTM D882	36.9	Mpa
					tensile strength	MD:Break,51μm	ASTM D882	32.6	Mpa
						tensile strength	TD:Break,20μm	ASTM D882	29.1	Mpa
						tensile strength	tensile strength	TD:Break,51μm	ASTM D882	32.4	Mpa
elongation	MD:Break,20μm	ASTM D882	500	%
	elongation	MD:Break,51μm	ASTM D882	660	%
		elongation	TD:Break,20μm	ASTM D882	710	%
		elongation	elongation	TD:Break,51μm	ASTM D882	710	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.