PA66 54G35HSL DUPONT USA

Form：Granules | Grade：Flame retardant grade

Properties:

High temperature resistanHigh resistanceGlass fiber reinforcedHigh rigiditywear resistantFiller: Glass fiber reinf35%Filler by weight

Typical Applications:

Electrical appliancesHousehold appliancesAutomotive interior parts

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical appliances \| Household appliances \| Automotive interior parts
Properties:	High temperature resistan \| High resistance \| Glass fiber reinforced \| High rigidity \| wear resistant \| Filler: Glass fiber reinf \| 35% \| Filler by weight

Certificates

No Data...

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	82	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11	kJ/m²
Tensile modulus	23°C	ISO 527-2	10500	Mpa
Elongation at Break	23°C	ISO 527-2	2.70	%
tensile strength	23°C	ISO 527-2	185	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	2E-05	cm/cm/°C
Vicat softening temperature	Melting Temperature	ISO 11357-3	300	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD2.0mm	ISO 294-4	0.50	%
Shrinkage rate	Shrinkage rate	MD2.0mm	ISO 294-4	0.20	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	相对漏电起痕指数	IEC 60112	575	V
Dielectric strength	0.250mm	IEC 60243-1	33	KV/mm
Volume resistivity		IEC 60093	>1.0E+15	Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.