Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 17 g/10min |
| melt mass-flow rate | | ISO 1133 | 24 g/10min |
| Shrinkage rate | | ASTM D955 | 0.40-0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.40-0.70 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 52.0 Mpa |
| tensile strength | | ISO 527-2/50 | 47.0 Mpa |
| elongation | | ASTM D638 | 22 % |
| elongation | | ISO 527-2/50 | 25 % |
| Flexural modulus | | ASTM D790 | 2200 Mpa |
| Flexural modulus | | ISO 178 | 2300 Mpa |
| bending strength | | ASTM D790 | 72.0 Mpa |
| bending strength | | ISO 178 | 65.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 7.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 15 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 60 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 85.0 °C |
| Heat distortion temperature | | ISO 75-2/A | 78.0 °C |
| vicat | | ASTM D15256 | 95.0 °C |
| vicat | | ISO 306/B50 | 96.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.