Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| density | | | 1.08到1.12 g/cm³ |
| Curing Time | | | 0.75到1.0 hr |
| STORAGE STABILITY | | | 7.0到9.0 min |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Resin | | 按重量计算的混合比:100 |
| Hardener | | 按重量计算的混合比:150 |
| | | 4.0 hr |
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| | ISO7619 | 76到80 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ISO178 | 2450到2750 MPa |
| Bending stress | | ISO178 | 73.0到83.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179 | 15到19 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 86.0到92.0 °C |
| Glass Transition Temperature | | TMA | 90.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.