Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.04 g/cm³ |
| Apparent density | | ASTM D1895 | 0.65 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 3.2 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 72 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | | ASTM D638 | 65 % |
| Flexural modulus | | ASTM D790 | 1900 MPa |
| bending strength | | ASTM D790 | 48.0 MPa |
| Tensile modulus | | ASTM D638 | 2050 MPa |
| tensile strength | | ASTM D638 | 24.0 MPa |
| tensile strength | | ASTM D638 | 29.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 110 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ASTM D15255 | 96.0 °C |
| Heat distortion temperature | | ASTM D648 | 90.0 °C |
| vicat | | ASTM D15254 | 103 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.