TPU-Est/eth DP R 3914 geba Kunststoffcompounds GmbH
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183/A | 1.36 g/cm³ | |
| Shrinkage rate | 0.11 % | ||
| 0.36 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 62 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | ISO 179/1eA | 20 kJ/m² | |
| ISO 179/1eA | 70 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 100 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| wear resistance | ISO 4649 | 65 mm³ | |
| tensile strength | ISO 527-2/200 | 58.0 MPa | |
| Tensile strain | Break | ISO 527-2/200 | 23 % |
| Flexural modulus | ISO 178 | 3620 MPa | |
| ISO 178 | 1370 MPa | ||
| bending strength | ISO 178 | 129 MPa | |
| ISO 178 | 43.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 162 °C | |
| ISO 75-2/A | 130 °C | ||
| vicat | ISO 306/B50 | 125 °C | |
| Linear coefficient of thermal expansion | DIN 53752 | 9E-06 cm/cm/°C | |
| DIN 53752 | 1.4E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.