Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 0.923 g/cm³ |
| melt mass-flow rate | | ISO1133 | 0.75 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Gloss | | ASTMD2457 | 85 |
| Haze ratio | | ASTMD1003 | 8.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Multi-AxialInstrumentedImpactEnergy | | ISO6603-2 | 2.50 J |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| | ISO8295 | 0.20 |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ISO527-3 | 24.0 MPa |
| elongation | | ISO527-3 | 250 % |
| elongation | | ISO527-3 | 550 % |
| Falling hammer impact | | ISO7765-1 | 120 g |
| Elmondov tear strength | | ISO6383-2 | 4.0 N |
| Elmondov tear strength | | ISO6383-2 | 2.0 N |
| Secant modulus MD | | ASTMD882A | 230 MPa |
| Secant modulus TD | | ASTMD882A | 260 MPa |
| tensile strength | | ISO527-3 | 27.0 MPa |
| Film thickness - tested | | | 40 µm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO11357-3 | 112 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.